			Siliziumkarbid
Materialeigenschaften	Norm	Symbol / Einheit	F	F plus	T
Dichte	DIN EN 623-2	ρ [g/cm3]	>3.10	>3.16	>3.21
Porosit?t	DIN EN 623-2	P [%]	<3.0	<1.0	<1.0
Mittlere Korngr??e		[μm]	<5	<5	<2
Korngr??enverteilung		[μm]
Phasenzusammensetzung			α-SiC	α-SiC	α-SiC, YAG
Vickers-H?rte	DIN EN 843-4	HV 1 [GPa]	25.5	25.5	22.5
Knoop hardness	DIN EN 843-4	HK 0.1 [GPa]	24.5	24.5	21.0
Young's modulus	DIN EN 843-2	E [GPa]	410	420	420
Weibull modulus	DIN EN 843-5	m	10	15	15
Flexural strength, 4-pt bending	DIN EN 843-1	σB [MPa]	400	510	550
Druckfestigkeit		σD [MPa]	2200	2200	2500
Poisson ratio		ν	0.17	0.17	0.16
Fracture toughness (SENB)		Klc [MPa·m0,5]	4	4	6
Coefficient of thermal expansion	DIN EN 821-1
20°C - 500°C		α [10-6/K]	4.1	4.1	3.5
500°C - 1000°C		α [10-6/K]	5.2	5.2	5.2
Spezifische W?rme bei 20°C	DIN EN 821-3	cp [J/g K]	0.6	0.6	0.6
W?rmeleitf?higkeit at 20°C	DIN EN 821-2	λ [W/mK]	125	125	75
W?rmebelastung Parameter	calculated
R1 = σB·(1-ν) / (α·E)		R1 [K]	198	246	314
R2 = R1·λ		R2 [W/mm]	25	31	24
Spezifische elektrische Widerstand bei 20°C	DIN EN 50359	ρ [Ω cm]	106-108	106-108	102-103

			Silicon Carbide
Material properties	Norm	Symbol/Unit	C	P	G
Density	DIN EN 623-2	ρ [g/cm3]	>3.10	>2.76- 2.89	>3.02
Porosity	DIN EN 623-2	P [%]	<3.0	10-14	<3.0
Mean grain size		[μm]	bimodal	<5	bimodal
Grain size distribution		[μm]	10-1500		10-1000
Phase composition			α-SiC	α-SiC	α-SiC, graphite
Vickers hardness	DIN EN 843-4	HV 1 [GPa]	25.5	23.5	24.5
Knoop hardness	DIN EN 843-4	HK 0.1 [GPa]	24.5	21.6	23.0
Young's modulus	DIN EN 843-2	E [GPa]	410	340	390
Weibull modulus	DIN EN 843-5	m	10	15	14
Flexural strength, 4-pt bending	DIN EN 843-1	σB [MPa]	400	225	230
Compressive strength		σD [MPa]	2500	2000	2500
Poisson ratio		ν	0.17	0.17	0.16
Fracture toughness (SENB)		Klc [MPa·m0,5]	3.5	3	3
Coefficient of thermal expansion	DIN EN 821-1
20°C - 500°C		α [10-6/K]	4.1	3.5	4.0
500°C - 1000°C		α [10-6/K]	5.2	5.6	5.0
Specific heat at 20°C	DIN EN 821-3	cp [J/g K]	0.6	0.6	0.6

Mehr Info>>

1.Hartmetall
2.Hartmetallkugeln
3.Hartmetallfr?ser
4.Hartmetalleins?tze
5.Hartmetallplatten

CHINATUNGSTEN ONLINE ist seit mehr als 20 Jahren auf die Herstellung von Wolframprodukten, insbesondere Hartmetallprodukten, spezialisiert. Wenn Sie Fragen zu den Produkten auf dieser Website haben, z?gern Sie nicht, uns eine E-Mail zu senden von:sales@chinatungsten.com